E2U Polyaspartics 85 Clear 2 Gallons

$202.00

E2U Polyaspartics is the next generation in two component, fast drying, Aliphatic Polyurea.

Clear
Questions about this product?
SKU: 9085CL-2 Categories: ,
Description

Description

E2U Polyaspartics is the next generation in two component, fast drying, Aliphatic Polyurea. While other Polyaspartics can only be applied between 8 and 10 mil, E2U Polyaspartic can be applied in a single coat up to 30 mils. It features good abrasion and chemical resistance, and a cure time of four to six hours. It can be installed in extremely high or low temperatures. It is the ideal product when low odor, fast turnaround and a non-yellowing system are essential.

Physical Properties
Volumetric Ratio: . . . . . . . . . . . . . . . . 1 to 1
Volumetric Solids . . . . . . . . . . . . . . . .. 85%
Coverage: . . . . . . . . . . 200 SF/Gal @ 8 mil
Application temperature: . . . . .35-100°F
Thinning: . . . . . . . . . . . . . . . . .Not required
Pot life: . . . . . . . . . . . . . . . . . 15-20 minutes
Working time on floor: . . 15-20 minutes
Cure time: . . . . . . . . . . . . . . . . . . .4-6 hours
Critical recoat time: . . . . . . . . . . . 12 hours
Shelf life: . . . . . . . . . . . . . . . . . . . 12 months
USDA Food & Beverage:. . . . Meets Req.

Color: Clear
Available Colors:

Clear Beige
Light Gray Tile Red
Medium Gray Safety Red
Dark Gray Safety Blue
White Safety Green
Black Safety Yellow
Tan

Packaging
2 Gallon Kit:
PartA . . . . . . . . . . . . . . . . . . . . . . . . . . .1 gal.
Part B. . . . . . . . . . . . . . . . . . . . . . . . . . .1 gal.
10 Gallon Kit:
PartA . . . . . . . . . . . . . . . . . . . . . . . . . . .5 gal.
Part B. . . . . . . . . . . . . . . . . . . . . . . . . . .5 gal.

PRODUCT LIMITATIONS
Ground level concrete slabs emit invisible moisture vapor. The allowable moisture emissions for concrete are 3 lbs / 1,000 SF over a 24 hour period. If moisture is above this level, then blistering and delamination of coating may occur. A calcium chloride test should be preformed to determine concrete moisture level. If moisture levels exceed the 3 lb. limit, a concrete moisture vapor control system should be used first before applying coating system. Please contact the technical department for approved systems. Coating systems are susceptible to cracking if the concrete moves or separates below the coating. Hence, joint and crack treatment should be reviewed prior to coating application.

As a general rule, control joints (saw cuts) and random cracks should be saw cut or chased first then filled with Easy Patch or similar approved hard epoxy product. Construction joints (two slabs which meet and hence move) should be treated. After the coating has been applied and cured, saw cut through the coating over construction joints and apply an elastodynamics caulking.

WARRANTY
E2U products are warranted for one year after date of application. Please refer to the Limited Material warranty for additional clarification.
SAFETY
Consult material safety data sheet. Avoid contact with skin. Some individuals may be allergic to epoxy resin. Protective gloves and clothing are recommended.
Applications

Applications

Pharmaceutical Food Prep/Kitchens
Garage Floors Restrooms
Manufacturing plants Aisle ways
Clean rooms Auto showrooms
Schools Laboratories
Basements Kennels
Veterinary facilities Locker rooms
Ramps Health Care facilities
Loading docks Car wash facilities
Advantages

Advantages

High Gloss & Build 4x more abrasion resistant than epoxy
Non-yellowing Chemically resistant
Low viscosity Easy mixing ration (1:1)
Solvent Free Cure at temperatures just above Freezing
High flowability
Typical Properties

Typical Properties

PROPERTY VALUE
Appearance Clear Liquid
Total Solids (% by Weight) 85
Total Solids (% by Volume) 85
Surface Tension, Dynes/cm 40
Viscosity (Brookfield LVF), cps @ 25° C 600
Density (lbs/gallon) 8.32
Specific Gravity 1.0
Flash Point (C Pensky-Martens closed cup) <70°F
Freeze/Thaw Stability N/A
Thermal Stability (28 days @ 52° C) No Effect
Mechanical Stability Good
VOC (g/l) 0
VOC (by Weight) 0
Tg (C) 66
Tensile Strength, psi 7000
Elongation 8%
Concrete Preparation

Concrete Preparation

Before coating is applied, concrete must be:
• Dry – No wet areas
• Clean – Contaminants removed
• Profiled – Surface etched
• Sound – All cracks and spalled areas repaired
Mechanical preparation is the preferred method of preparing concrete for coat- ing application. Shot-blasting, diamond grinding, scarifying and scabbling are all acceptable methods

Patching

Patching

Voids, cracks and imperfections will be seen in finished coating if the concrete is not patched correctly. Patch concrete with Easy Patch. After the patching material is cured, diamond grind patch. If a non-patching material is used, contact a technical representative for a compatible and approved alternative.

Testing

Testing

All surfaces are not the same. It is recommended that a sample area be done before the start of the project. The test should be done on-site, using the pro- posed method by the assigned applicator to insure proper adhesion and color. A sample area should also be done on any existing coatings to determine if any contaminants exist or if delaminating will occur.

Mixing

Mixing

The ratio of Polyaspartic 85 is 1 to 1. 1 part A (resin) to 1 part B (hardener). Generally, one mixed gallon is ideal for application. Mix the following with a stir stick. Note: If using a drill mixer, use a low speed to prevent air entrapment.
1. Pour out 1/2 gallon of Part A into a clean bucket.
2. Add 1/2 gallon of Part B and mix for 2 minutes.
**Do not store product in direct sunlight

Clean Up

Clean Up

While in an un-reacted state, may be cleaned up with water and degreaser. Isopropyl alcohol or acetone may be needed once the resin begins hardening. Lastly, a strong solvent like methylene chloride may be required if resin is nearly set up.

Film Properties

Film Properties

PHYSICAL PERFORMANCE PROPERTIES OF DRY FILM
All tests were conducted on 2.0 to 2.5 mil films, and air-dried for seven days at room temperature.

PROPERTY VALUE
Hardness (Pencil / Sword) 2H / 70
Taber Abrasion (mg loss per 1000 cycles, CS-17 wheel, 1000 load) 90
Impact Resistance (Direct / Reverse) 140 / 140 (lbs)
Crosshatch Adhesion (Untreated Cold Rolled Steel / Untreated Aluminum) 100% / 100%

QUV WEATHEROMETER (ALCLAD ALUMINUM 1000 HRS.)

PROPERTY VALUE
Oxidation No Effect
Loss of Gloss Slight

CHEMICAL RESISTANCE: 7-DAY SUBMERSION

PROPERTY VALUE
Brake Fluid No Effect
Transmission Fluid Slight Discoloration
Coolant No Effect
Power Steering Fluid Slight Discoloration
Battery Acid Damaged
MEK  <200 Double Rubs
Acetone  <200 Double Rubs
Formula 409  <200 Double Rubs
Datasheet